Field Applied Joint Epoxy for Plant Coated Pipe


TC® 7010 Fast Set Epoxyis a high-build, surface tolerant coating that exceeds all performance criteria for the protection from corrosion of above and below groundpipelines.

TC 7010 provides exceptional corrosion prevention for protecting joints, patching pipeline coatings, and covering irregular fittings and metal surfaces. This innovative product can be used in conjunction with all factory and field coatings, such as cold and hot applied tape, coal tar enamel, extruded polyethylene, and fusion bonded epoxy.

TC 7010 Fast Set Epoxy is a two part liquid epoxy system. Used as a one-coat stand-alone protective coating system for above and below grade application on dry substrates.

Tapecoat 7010 Fast Set Gray Epoxy eliminates the complex and lengthy application process required for field-applied powder epoxy coating of welded joints.

TC 7010 is an environment friendly two component, 100% solids material that provides up to 30 mils of high-build thickness for tough abrasion resistance to backfill and soil stress damage. This fast set epoxy also decreases lengthy field application by accepting backfill after only 2 hours of cure time.

Please click here for TC 7010 PDF Product Sheet.

TECHNICAL SPECIFICATIONS


Basic Use
TC 7010 FS-Gray is a corrosion preventive epoxy coating developed for coating joints, patching pipeline coatings and coating irregular fittings and surfaces; suitable for above and below ground applications.

Composition
TC 7010 FS-Gray Epoxy is a modified amine cured epoxy coating with 100% solids content.


Technical Data: (at 20 mils)
VOC: 0 lbx/gal (0 kg/l)/(.5mm)

Solids: 100% by volume
Coverage: 80 ft2/gal (20 mils)/(1.96 m2/liter) (.5mm)

Color: Gray
Curing time @ 70°F: 2 hours to backfill
Applications temp: 40-120°F (4--49°C)
Operating temp: -40 to 165°F (-40 to 740C)
Thickness: 20 mils (.5 mm)
Weight per gallon: 12 lbs. (5.4kg)

Surface Preparation
Remove all contaminants that would impede bond. Use effective cleaning procedures to remove: moisture, salts, rust, dirt and dust, oil and grease. This may include the
use of high pressure fresh water cleaning, using suitable solvents or detergents to SSPC-SP-1 or abrasive blast to SSPC-SP-6.

Application
Environment: Use only where application and curing can proceed at temperatures above 40°F (40°C). The temperature of the surface and that of the coating itself must also be within these limits. Apply only on a dry and clean surface with a temperature above the dew point to avoid condensation. Relative humidity maximum is 90% preferably between 40-60% (See detailed field specificatons for complete instructions.)
Mixing: Pour entire contents of Part A and Part B into a separate container (furnished in the kit) and mix thoroughly until homogenously mixed, approx. 2-3 minutes.
Application Method: Apply epoxy by brush, pad or roller.